STUDI PEMBUATAN KERAMIK BERPORI BERBASIS CLAY DAN KAOLIN ALAM DENGAN ADITIF ABU SEKAM PADI

Henok Siagian, Martha Hutabalian

Abstract


This research aims to make clay and Pahae natural kaolin based porous
ceramic using hull of rice ash as additive and tu study the influence of variation of
composition of hull of rice additive with clay and Pahae natural kaolin to the
characteristics of porous ceramic on sintering temperature 9ooac, 10ooac, and
11000C.
The raw material of this ceramic consists of clay and Pahae kaolin mixing with the
addition of hull of rice ash as additive in the percentage 0%, 5%, 10% and 15% and
then sintering of each admixture in temperature of 9000C, 1000°C and 1100°C. This
aims to get the better admixture by burning and to study whether is there an
increasing of physical characteristics of the porous ceramic material, i.e. burning
wastage, porosity, density, hardness and XRD (X-Ray Diffraction) analysis.
Based on the results of research indicates that the physical characteristics of clay and
Pahae natural kaolin based porous ceramic with hull of rice ash as additive is : the
burning waste on sintering temperature 900°C-11000C is (18.91 - 23.31)%, the
porosity value is (27.80 - 56.94)%, density value is (1.33 - 1.71) gr!cm3, hardness
value is (8.78 - 12.87) kgflmm2 and the results of XRD analisys indicates that the
dominant phase on ceramic is Aluminium Silicate Hydroxide [Al2Si20s(OH)4].


Keywords


Keramik berpori, Clay dan Kaolin, Abu sekam padi, Sifat ft.sis

Full Text:

PDF

References


Anggono, dkk. (2008), Penyusutan Dan

Densifikasi Keramik Alumina:

Perbandingan Antara Hasil Proses Slip

Casting Dengan Reaction Bonding,

Jurusan Teknik Mesin-Fakultas

Teknologi Industri, Universitas

Kristen Petra.

Astuti, A. (1997), Pengetahuan Keramik, Gajah

Mada University Press, Yogyakarta.

Fitria , A T. (2008), Pemanfaatan Limbah

Sandblasting dan Clay PT.Pertamina

UP IV Cilacap Sebagai Bahan

Pembuatan Keramik Dengan Metode

Solidifikasi.

http://rac.uii.ac.id/server/document/

private/20080605124910skripsi.pdf

Harefa, F.B. (2009), Pemanfaatan Limbah Padat

Pulp Grits Dan Dregs Dengan

Penambahan Kaolin Sebagai Bahan

Pembuatan Keramik Konstruksi,

Jurusan Fisika FMIPA, USU, Medan.

Joskar. (2009), Pembuatan Keramik Berpori

Dari Limbah Padat Pulp Dengan Aditif

Kaolin Sebagai Filter Gas Buang,

Pascasarjana USU, Medan.

Pasaribu, H. (2010), Preparasi dan

Karakterisasi Bahan Keramik Berpori

Berbasis Clay dan Feldspar Dengan

aditif Sekam Padi, Jurusan Fisika

FMIPA Unimed, Medan.

Sembiring, A.O. (1995), Pembuatan Keramik

Berpori Dengan Menggunakan Karban Aktif Sebagai Aditifnya, Jurusan

Fisika FMIP A, USU, Medan.

Sihite, D.R. (2008), Pembuatan dan

Karakterisasi Bohan Keramik Berpori

Dengan Aditif Sekam Padi Yang

Digunakan Sebagai Filter Gas Buang,

Pascasarjana USU, Medan.

Tarnbunan, T.D. (2008), Pembuatan Keramik

Berpori Sebagai Filter Gas Buang

Dengan Aditif Karban Aktif,

Pascasarjana USU, Medan.

Tobing, H. (2009), Pengaruh Penambahan Abu

Sekam Padi dan Suhu Sintering

Terhadap Karakterisasi Keramik Berpori

Berbasis Zeolit Alam Pahae, Jurusan

Fisika FMIP A Unirned, Medan.

Tobing, N. (2009), Preparasi Dan Karakterisasi

Keramik Clay Dengan Silika Sekam

Padi Menggunakan Teknik Sintering,

Jurusan Fisika FMIP A Unirned,

Medan.

VanVlack, L.H., (1992), Ilmu Dan Teknologi

Bohan, Penerbit Erlangga, Jakarta.


Article Metrics

Abstract view : 326 times
PDF - 3345 times

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.
slot gacor slot